In April 2016 Manchester eScholar was replaced by the University of Manchester’s new Research Information Management System, Pure. In the autumn the University’s research outputs will be available to search and browse via a new Research Portal. Until then the University’s full publication record can be accessed via a temporary portal and the old eScholar content is available to search and browse via this archive.

Corrosion Behaviour of Extruded Heat Exchanger Aluminium Alloys

Laferrere, Alice Marie

[Thesis]. Manchester, UK: The University of Manchester; 2012.

Access to files

Abstract

Extruded Al-Mn alloy are used in heat exchanger applications due to their light weight and good thermal conductivity. Depending on the application, the units may be subjected to external corrosion, which can lead to perforation of the tube. The industrial test most commonly used to assess heat exchanger alloys is the seawater acetic acid test (SWAAT). This is a cyclic fog at 40°C and pH 2.9. In the present study, it was found that pits developing in extruded Al-Mn tubes during the SWAAT test are purely crystallographic. Furthermore, a mechanistic understanding for crystallographic pitting has been developed. The SWAAT test can be of relatively long duration and, typically, does not yield information on the underlying corrosion initiation and propagation mechanisms. In the present study, alternate methods to assess pitting corrosion were elaborated. A drop testing procedure has been successfully implemented to study the mechanism of pit initiation. It was revealed that pits initiated within the aluminium matrix in the vicinity of grain boundaries. A close link between large second-phase particles and pit initiation was established. No preferred grain orientation for pit initiation was evident.Scanning electron microscopy and associated tomography were undertaken for the first time to clarify the mechanism of pit propagation. The pit walls were oriented {100}, while the fast-dissolving planes were {110} and {111}. The findings were in accordance with previous literature. Corrosion penetrated deeper into the alloy when the corrosion front was close to a grain boundary. Pit walls were cathodic to the aluminium matrix, possibly due to enrichment of alloying elements at pit walls.The effect of alloy additions on the corrosion behaviour of extruded aluminium alloys was investigated. Alloys with varying copper, iron and manganese contents were compared. Shot noise analysis and post-mortem analyses were undertaken. The increased amount of manganese in solid solution delayed the transition from micropits to stable pitting. This delay is attributable to second-phase particles that are less cathodic to the aluminium matrix in alloys with increased manganese content. Increasing copper decreased the size of the dissolved polyhedra during stable pitting. Furthermore, pits propagated faster in alloys rich in copper. This could be attributed to an increased level of copper enrichment at the pit walls. Finally, more second-phase particles were present in alloys with increased iron levels. Additionally, pits located in those alloys propagated deeper than pits located in alloys with low levels of iron. A competition between two different types of cathodes, enrichment layer and second-phase particles, is suggested.In conclusion, the effect of microstructure and alloy additions on the corrosion mechanism for crystallographic pitting developed during the project was clarified.

Bibliographic metadata

Type of resource:
Content type:
Form of thesis:
Type of submission:
Degree type:
Doctor of Philosophy
Degree programme:
PhD Materials
Publication date:
Location:
Manchester, UK
Total pages:
234
Abstract:
Extruded Al-Mn alloy are used in heat exchanger applications due to their light weight and good thermal conductivity. Depending on the application, the units may be subjected to external corrosion, which can lead to perforation of the tube. The industrial test most commonly used to assess heat exchanger alloys is the seawater acetic acid test (SWAAT). This is a cyclic fog at 40°C and pH 2.9. In the present study, it was found that pits developing in extruded Al-Mn tubes during the SWAAT test are purely crystallographic. Furthermore, a mechanistic understanding for crystallographic pitting has been developed. The SWAAT test can be of relatively long duration and, typically, does not yield information on the underlying corrosion initiation and propagation mechanisms. In the present study, alternate methods to assess pitting corrosion were elaborated. A drop testing procedure has been successfully implemented to study the mechanism of pit initiation. It was revealed that pits initiated within the aluminium matrix in the vicinity of grain boundaries. A close link between large second-phase particles and pit initiation was established. No preferred grain orientation for pit initiation was evident.Scanning electron microscopy and associated tomography were undertaken for the first time to clarify the mechanism of pit propagation. The pit walls were oriented {100}, while the fast-dissolving planes were {110} and {111}. The findings were in accordance with previous literature. Corrosion penetrated deeper into the alloy when the corrosion front was close to a grain boundary. Pit walls were cathodic to the aluminium matrix, possibly due to enrichment of alloying elements at pit walls.The effect of alloy additions on the corrosion behaviour of extruded aluminium alloys was investigated. Alloys with varying copper, iron and manganese contents were compared. Shot noise analysis and post-mortem analyses were undertaken. The increased amount of manganese in solid solution delayed the transition from micropits to stable pitting. This delay is attributable to second-phase particles that are less cathodic to the aluminium matrix in alloys with increased manganese content. Increasing copper decreased the size of the dissolved polyhedra during stable pitting. Furthermore, pits propagated faster in alloys rich in copper. This could be attributed to an increased level of copper enrichment at the pit walls. Finally, more second-phase particles were present in alloys with increased iron levels. Additionally, pits located in those alloys propagated deeper than pits located in alloys with low levels of iron. A competition between two different types of cathodes, enrichment layer and second-phase particles, is suggested.In conclusion, the effect of microstructure and alloy additions on the corrosion mechanism for crystallographic pitting developed during the project was clarified.
Thesis main supervisor(s):
Funder(s):
Language:
en

Institutional metadata

University researcher(s):

Record metadata

Manchester eScholar ID:
uk-ac-man-scw:158203
Created by:
Laferrere, Alice
Created:
29th March, 2012, 10:32:48
Last modified by:
Laferrere, Alice
Last modified:
23rd May, 2012, 19:30:35

Can we help?

The library chat service will be available from 11am-3pm Monday to Friday (excluding Bank Holidays). You can also email your enquiry to us.